Die Life of cold stamping die and mprovements

Overview of stamping die  

Stamping Die - Stamping in the cold, the material (metal or non-metallic) processing into parts (or half) of a special technical equipment, called cold stamping die (commonly known as Die). Press - is at room temperature, using the die installed in the press to put pressure on the material to produce a separation or plastic deformation, and thus to obtain the necessary parts of a pressure processing method. Stamping die in the form of many, the general categories according tothe following main features: 

1. According to the technical nature of  

2. According to the degree classification process combination  

Chong called cold stamping die Die-wide.  

Cold stamping die is used in cold stamping die mold industry, and accessories required for high-performance structural ceramic materials, preparation methods, high-performance ceramic materials, molds and accessories from the zirconium oxide and yttrium aluminum powder increases, Pr element composition, Preparation is the solution of zirconia, yttria solution, praseodymium oxide solution, according to a certain percentage of alumina solution when mixed liquor, ammonium bicarbonate infusion, by co-precipitation synthesis of ceramic materials, molds and accessories needed for raw materials, reaction precipitate generated by the treatment, drying, calcining and accessories by highperformance ceramic mold material superfine powder, and then after forming, sintering, finishing, they will have high-performance ceramic materials, molds and accessories. Advantages of this invention is the invention made of cold stamping dies and parts and long service life, the process does not appear in the press and its parts and stamping die bond generated the phenomenon of stamping surface is smooth, no glitches, can replace traditional high-speed steel, tungsten steel. 

Die with the main parts  

Die stamping tools is the main process equipment, stamping rely on the relative movement under the mold completed. Processing time because the upper and lower mold between the constant division and, if continued operation of the fingers of workers to enter or remain in the mold closed, there will certainly pose a serious threat to their personal safety.    

1. Working parts is a direct punch to blank forming the working part, therefore, it is the key to mold parts. Punch not only sophisticated and complex.  

2. Positioning parts positioning part is to determine the location of the parts installed blank, there are pins (board), gauge pin (plate), lead is sold, guide plate, knife set from the side, side pressure etc.. Design should be considered when positioning parts easy to operate and should not have had orientation, location to facilitate observation, preferably in the forward position, contouring to correct the pin location and positioning.  

3. Binder, unloading and discharging parts binder components are blank holder, binder board. 

4. Guide parts and guide sleeve guide pin is the most widely used part of a guide. Its role is to ensure punch the punching clearance when accurate match. Therefore, the guide posts, guide cover the gap should be less than the blanking clearance. Guide Post located next mold base, to ensure that the stroke bottom dead center, the lead column in the template on the face over the top for at least 5 to 10 mm. Guide columns should be arranged far away from the module and the pressure plate in the area, so the operator's arms do not get to take over the lead column material.

5. Supporting and clamping the upper and lower parts which includes templates, die handle, fixed plate punch, plate, stopper, etc..   Up and down the template is the basis of the cold die parts, other parts are respectively fixed at the top. Template plane size, especially around the direction to be compatible with the workpiece, too large or too small are not conducive to action.  

6. Fastening parts which includes screws, nuts, springs, pins, washers, etc., are generally used standard parts. Die more with the amount of standard parts, design choice and flexibility should be tightened to ensure the top out of the need to avoid exposure to the surface fastener operating position, the staff and impede operation to prevent bumps.   

Die with the development of  

Since reform and opening, with the rapid development of the national economy, the market demand with the growing Die. In recent years, Die with the industry hasbeen around 15% growth rate of the rapid development of industrial enterprises with ownership Die components also changed dramatically, in addition to the professional mold factory outside of state-owned, collective, joint ventures, wholly-owned and private has been a rapid development.  

Die with enterprises to increase in recent years many technological advances for investment, technological progress will be seen as an important driving force for enterprise development. Some domestic enterprises have popularized the two-dimensional mold CAD, and gradually began to use UG, Pro / Engineer, I-DEAS, Euclid-IS and other international common software, individual manufacturers have also introduced Moldflow, C-Flow, DYNAFORM, Optris and MAGMASOFT etc. CAE software, and successfully applied in stamping die design.      

1. cold stamping technology process parameters should be properly identified and Die with the work of some of the shape and size, to improve the quality of stamping parts and shorten the new product production cycle should be in strengthening the metal forming the basis of theoretical studies, to metal forming theory to practice can produce a direction, and gradually establish a close connection with the actual production of the advanced process of calculation. abroad have begun to use plastic finite element method, automobile parts forming process of the stress and strain analysis and computer simulation to predict the forming part of a process plan on the possibilities and potential problems.  

2. to accelerate product replacement, mold design to overcome the shortcomings of a long cycle. Should vigorously carry out computer-aided design and manufacture of molds (CAD / CAM) Research. In my country, paying particular attention to strengthening the multi-position progressive die CAD / CAM Technology. 

3. to meet the needs of mass production, and reduce labor intensity. Should strengthen cold stamping of mechanized and automated, so that the average, small pieces of high-speed presses in a multi-position progressive die production, production reached a high degree of automation to further improve stamping productivity. 

Die with life and Countermeasures  

Die with the life of the workpiece by punching out the number of terms. Many factors affect the life Die. There are die structure design, manufacture molds used in the punch and die materials, die quality and surface hardening heat treatment, precision die manufacturing parts and cold stamping materials selection. In addition, there are die installation, adjustment, use and maintenance. 

  1. Die Design on Life  

(1) Layout design of layout methods and take the boundary value a great impact on the die life, too small to take the boundary value, often causing rapid wear and convex mold, die bite wounds on the. Starting from material savings, take the boundary value smaller the better, but take the edge is less than some value, the cut surface of themold and the quality of life adversely. There will be left behind in the blanking die Q-gap were to produce spare parts glitch, or even damage the die edge, reduce die life. Therefore, consider increasing the material utilization of the same time, parts must yield, quality and life expectancy to determine the layout methods and take the boundary.  

(2) die structure prone to stress concentration on the cracking of the die structure, composite structure can be used or mosaic structure, and prestressed structure to enhance the mold life.  

  2. Die Die Life of 

  Die Die Life of a mold material propertie, chemical composition, structure, hardness and comprehensive reflection of metallurgical quality. Among them, the material properties and heat treatment affect the quality of the most obvious. Mold material properties on the impact of die life is great. If the same workpiece, using a different mold material of the bending test, the test results: The 9Mn2V material, the life of 5 million; with Crl2MoV nitriding, the life of up to 40 million. Therefore, the choice of materials, the batch size should be based on workpiece, rational use of mold materials. The hardness of the die parts to Die Life a great impact. But not the higher hardness, longer die life. This is because the hardness and strength, toughness and abrasion resistance are closely related. Some die demands of high hardness, long life. Such as the use of T10 steel dies, hardness 54 ~ 58HRC, only washed thousands of times a burr on the workpiece great. If the hardness to 60 ~ 64HRC, the grinding life of up to 2 to 3 million. However, if continue to improve hardness, fracture occurs earlier. Some die hardness should not be too high, as the die manufacturing using Crl2MoV 58 ~ 62HRC hardness, the general life of 2-3 million, invalid form of chipping and cracking, and if the hardness down to 54 ~ 58HRC, life expectancy increased to 5 ~ 60 000, but decreased to 50 ~ 53HRC hardness appear easy to blunt the die edge phenomenon. Thus, mold hardness must be based on material properties and failure modes may be. Should enable the hardness, strength, toughness and wear resistance, resistance to fatigue strength needed to achieve a particular stamping process the best match.

   3. The surface of the mold heat treatment to strengthen the quality and impact on life  

  4. Manufacturing precision of the die parts of die life   Precision die manufacturing and life in it in particular, mold surface roughness on the mold a great impact. If using Crl2MoV steel blanking die, if the surface roughness value R = 1.6 m, its life span is about 30,000. Such as polished by the precision, surface roughness value R = 0.4 m, life can be increased to 4-5 million. Therefore, the working parts of the mold surface, the general must go through grinding, grinding, polishing and other finishing and fine processing. 

  5. Other aspects of the impact of die life  

 6. Conclusion   In actual production, sheet metal dies for use, rare case of non-normal wear and tear. But when the die plate was found prone to irregular wear, we always study for the problems summarized. Because of a cold die, from the design, manufacture, assembly, commissioning and installation and use, all spent many hours, while the convex die, die material used, mostly high-quality alloy steel. Therefore, the die cost is relatively high. Therefore, in the production of understanding the factors that affect the die life and take the appropriate measures to guide the production of great practical significance.